PFTG 韩国sk K2012
产品参数
PETG韩国SKK2012 物性数据表
·
性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
机械性能 | 拉伸强度(引张强度) | ASTM D412/ISO 527 | kg/cm2(MPa)[Lb/in2] | ||
断裂伸长率 | ASTM D412/ISO 527 | 70 | % | ||
拉伸模量 | ASTM D412/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
拉伸屈服伸长率(延伸率) | ASTM D412/ISO 527 | % | |||
拉伸断裂伸长率(延伸率) | ASTM D412/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | 2150 | kg/cm2(MPa)[Lb/in2] | ||
弯曲强度 | ASTM D790/ISO 178 | 80 | kg/cm2(MPa)[Lb/in2] | ||
洛氏硬度 | ASTM D785 | 116 | kg·cm/cm(J/M)ft·lb/in | ||
IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
1/4" -30℃ | ASTM D256/ISO 179 | kg/cm2(MPa)[Lb/in2] | |||
1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
-30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
23℃（无缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
-30℃（无缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.27 | ||
成型收缩率 | ASTM D955 | 0.2 | % | ||
光学性能 | 折射率 | ASTM D542/ISO 489 | 1.570 | ||
透光率 | ASTM D1003/ISO 13468 | 89.0 | % | ||
模糊系数（Haze） | ISO 14782 | % | |||
其他 | 备注 | ||||
颜色 | GT | ||||
特性 | 高光泽，耐化学，食品级，韧性良好，可加工性良好 | ||||
用途 | 电气/电子应用领域，护罩，玩具，片材，瓶子，医疗/护理领域 | ||||
3D打印专用材料/韩国SK PETG K2012
韩国SK PETG K2012 是3D打印的专用材料
出众的热成型性能
PETG板材易于生产出造型复杂及拉伸比大的制品。而且，与PC板和抗冲改性的压克力不同，这种板材无须在热成型加工前进行预干燥处理。与PC板或压克力相比，其成型周期短，温度低，成品率更高。
坚韧性
PETG板材的挤出板材通常比通用压克力坚韧15至20倍，比抗冲改性的压克力坚韧5至10倍。PETG板材在加工、运输和使用过程中具有足够的承受能力，有助于防止破裂。
耐候性
PETG板材提供了的耐候性。它可以保持产品的坚韧性，防止变黄。它含有紫外线吸收剂，可共挤成一保护层，保护了板材免受紫外线的有害影响。
加工简便
PETG板材可进行锯切、模切、钻孔、冲孔、剪切、铆接、铣边以及冷弯，不至于破碎。表面的轻微刮痕可用热风枪来消除。溶剂粘接亦是常规操作。它比通用压克力、抗冲改性压克力或PC板更易于加工，并可进行植绒、电镀、静电等加工处理。
的耐化学性能
PETG板材可以耐受多种化学品以及常用的清洁剂。
环保
PETG板材基材均为环保材料，符合食品接触管理要求。
经济性
它比PC板便宜，比压克力经久耐用。